熔体质量流动速率(MFR):(190°C/2.16 kg)断裂伸长率:50 mm/min,3.2mm规格:原厂原包报价方式:以实际订单报价为准是否进口:是熔点:77.2℃材料:EAA分子量:20.5%订货时间:现货供应名称:乙烯丙烯酸共聚物应用:饮料纸盒 密封材料 牙膏管 等等
产品说明
PRIMACOR 3004 is an ethylene acrylic acid copolymer designed for extrusion/coextrusion coating and laminating. It provides excellent hot tack
and adhesion to metallic, paper and polyethylene substrates with excellent heat seal strength, even through many oil and powdered products. This
resin also offers outstanding resistance to delamination, as well as excellent toughness and environmental stress crack resistance (ESCR).
Excellent draw down and edge stability
Excellent product resistance
Excellent hot tack, heat seal, toughness
High performance sealant or tie layer
Complies with:
U.S. FDA 21 CFR 177.1310(b)
EU, No 10/2011
Consult the regulations for complete details.
挤压说明
挤出涂层薄膜的制造条件:
用于处理此树脂的设备应由***材料制成。建议模具和适配器采用不锈钢和/或双面镀铬或镀镍。
螺杆尺寸:3.5 英寸 (89 mm);30:1 L/D
模具:30 英寸模具切边至 24 英寸
模具间隙:20 密尔 (0.508 mm)
熔体温度:550°F (288°C)
输出:250 磅/小时
气隙:6 英寸 (152 mm)
备注 1 一般属性:这些不能被视为规格。
2 如同在生产时测量的一样。
总体
材料状态 已商用:当前有效
供货地区 亚太地区
机构评级 EU No 10/2011 FDA 21 CFR 177.1310 (b)
形式 颗粒料
物理性能 额定值 单位制 测试方法
比重 0.938 g/cm ASTM D792
ISO 1183
熔流率 2 (190°C/2.16 kg) 8.5 g/10 min ASTM D1238
ISO 1133
共聚单体含量 3 9.7 %
机械性能 额定值 单位制 测试方法
抗张强度 ASTM D638
ISO 527-2
屈服, 模压成型 7.93 MPa
断裂, 模压成型 17.6 MPa
伸长率 (断裂, 模压成型) 600 % ASTM D638
ISO 527-2
热性能 额定值 单位制 测试方法
维卡软化温度 81.1 °C ASTM D1525
ISO 306
溶融温度(DSC) 98.0 °C Internal Method
挤出 额定值 单位制 测试方法
熔体温度 260 到 290 °C
内缩量 (288°C, 25.4 m) 50.8 mm Internal Method
小涂层厚度 10 m Internal Method
小涂层重量 9.8 g/m Internal Method
EAA优良的热稳定性,颜料着色力优异,对各种基材都具有粘结力,这些基材包括金属、聚烯烃、纤维素、聚酯、聚碳酸酯、聚偏二氯乙稀(PVDC)、玻璃和金属箔等。主要应用于包装、粉末涂层、粘合剂、热熔胶、密封材料、水性溶剂,环保降解材料等方面。
挤出级一 简介:乙烯丙烯酸共聚物(Ethylene Acrylic Acid 简称EAA)是一种具有热塑性和高粘接性的聚合物,由于羧基团的存在以及氢键的作用,聚合物的结晶化被抑制,主链的线性被破坏,因此提高了EAA的透明性和韧性,降低了熔点和软化点。